Euclid Ultrasil LI+: Concrete Sealer 5 Gallon

Euclid Ultrasil LI+: Concrete Sealer 5 Gallon

Euclid Ultrasil Li+ is a water-based lithium silicate solution used to densify, seal and dustproof concrete surfaces. Euclid Ultrasil LI+ penetrates and chemically reacts within the concrete surface, producing extremely hard and dense calcium silicate hydrate (CSH) in the pores. The result is concrete that is more durable, easier to clean, and more resistant to damage from water and mild chemicals. Because the product of the lithium silicateconcrete reaction is formed internally, the protection of ULTRASIL LI+ never peels or flakes off, is unaffected by moisture, and lasts much longer than surface sealers and coatings. Questions? Contact Us.

Primary Applications:                                                                                                                                                                                                                    • Interior concrete floors
• Commercial and retail floors
• Diamond polishing concrete
• Warehouse floors
• Manufacturing plants
• Distribution centers
• Transportation terminals
• Institutional floors
• Health care facilities
• Clean rooms
• Mechanical rooms

Directions for Use:
ULTRASIL LI+ should be used directly from the container and requires no dilution or pre-mixing.

Surface Preparation (New Concrete): Cure the concrete by a wet or sheet cure method in accordance with ASTM C171, or with a curing compound that meets the requirements of ASTM C309. Euclid Chemical’s dissipating curing compound KUREZ DR VOX is recommended. To maximize strength and other physical properties of the concrete slab, new concrete should cure seven days or longer before application of ULTRASIL LI+. For fast track projects, the cure time may be reduced at the discretion of the project engineer. If a curing compound is used, it must be completely removed before application of ULTRASIL LI+. Surfaces to be treated with ULTRASIL
LI+ must be clean, dry and absorbent. Surface Preparation (Existing/Older Concrete): Concrete must be clean and free of any materials that could prevent penetration of ULTRASIL LI+, such as curing compounds or cure & seals, paints, coatings, dirt/oil, waxes, etc. If necessary, use EUCO CLEAN & STRIP to remove these contaminants before applying ULTRASIL LI+.

Application (New or Old Concrete): Air temperature during application must be between 35°F and 100°F (2°C and 38°C) for proper chemical reaction of the ULTRASIL LI+. Apply a single coat of ULTRASIL LI+ using a low pressure sprayer equipped with a 0.5 gal/min (1.9 L/min) spray tip. Apply at a coverage rate that results in a uniformly wet surface without puddles. While ULTRASIL LI+ is still wet, use a soft-bristle broom or microfiber pad to redistribute and evenly spread out the material. Do not continue to brush or spread out ULTRASIL LI+ once the product begins to dry. Keep the floor wet with ULTRASIL LI+ for 5-10 minutes. Do not allow excess ULTRASIL LI+ to puddle and dry on the floor. This may result in a white residue that must be removed immediately with scrubbing. If immediate surface sheen is desired, dry buff or burnish the floor with a polishing pad appropriate for the desired end gloss result.

Floor Joints: If the floor joints are to be filled after ULTRASIL LI+ has been applied, they must be thoroughly cleaned before installation of joint filler. Cleaning joints by circular concrete saw or a grinder equipped with a wire wheel is recommended.

Euclid